Thickly grated colored oil paints. Specifications

GOST 8292-85

GOST 8292-85 Group L18

STATE STANDARD SOYU3A SSR

OIL PAINTS, COLORED, THICKLY GRATED Technical specifications Oil and paste color paints. Specifications

OKP 23 1710

Date of introduction 1987-01-01

INFORMATION DATA

1. DEVELOPED AND INTRODUCED by the Ministry of Chemical Industry DEVELOPERS

V.B. Manerov, V.M. Makarova, I.P. Gnezdova, L.V. Kozlov, V.V. Sashevsky

2. APPROVED AND ENTERED INTO EFFECT by Resolution of the USSR State Committee on Standards dated December 18, 1985 N 4158

3. Inspection frequency: once every five years

4. INSTEAD OF GOST 695-77, GOST 8292-75 and GOST 8866-75* __________________ * The text of GOST 8292-85 (official publication - M.: Standards Publishing House, 1986) provides information about the cancellation of GOST 8866-76. — Note.

5. REFERENCE REGULATIVE AND TECHNICAL DOCUMENTS

6. The validity period was removed by Decree of the USSR State Standard of December 27, 1991 N 2237

7. REISSUE (June 1994) with Amendment No. 1, approved in December 1991 (IUS 4-92)

This standard applies to thickly ground oil colored paints, which are a paste consisting of pigments and fillers or the corresponding pigment (iron lead according to GOST 8135-74, mummy, ocher), rubbed on drying oil with or without the introduction of a drier. The paints, after being diluted with drying oil to a painting consistency, are intended for finishing work and for painting metal and wooden products used indoors and in atmospheric conditions in areas with a temperate climate. Coatings with thickly rubbed oil colored paints intended for use in atmospheric conditions, in two layers on metal, retain protective properties in a temperate climate for 1.5 years up to a score of no more than A32. Protective properties are assessed according to GOST 9.407-84. Paints are applied to the surface with a brush, roller or pneumatic spraying. The requirements of paragraphs 8 and 9 of Table 2 are recommended. The remaining requirements of the standard are mandatory. (Changed edition, Amendment No. 1).

TECHNICAL REQUIREMENTS

1. TECHNICAL REQUIREMENTS

1.1. Depending on the purpose, oil-based thickened paints are produced in the brands and colors indicated in Table 1, with the corresponding OKP codes.

Table 1

1.2. Thickly ground oil paints must be manufactured in accordance with the requirements of this standard according to the recipe and technological regulations approved in the prescribed manner.

1.3. Before use, thickly ground oil paints are diluted with drying oils in an amount of 20-30% (for brands MA-015 and MA-025) and 30-40% (for brands MA-015 red lead, MA-015 mummy, MA-015 ocher) by weight thick rubbed paint. Paints of brands MA-015, MA-015 red lead, MA-015 mummy, MA-015 ocher are diluted with natural drying oils (GOST 7931-76) or combined K-3, K-5. Paints of the MA-025 brand are diluted with natural drying oils, “Oxol” (GOST 190-78) or combined K-2, K-3, K-5. Before use, it is allowed to dilute paints of the brands MA-015, MA-015 red lead, MA-015 mummy, MA-015 ocher with Oxol drying oil, and the paints are used only for indoor coatings.

1.4. After dilution with drying oil, paints are, if necessary, diluted with white spirit (nefras -155/200) (GOST 3134-78) in an amount of no more than 5% by weight of the paint.

1.3, 1.4. (Changed edition, Revised, No. 1).

1.5. When using ocher, up to 2% of NF-1 grade (GOST 1003-73) or ZhK-1 grade drier is added by weight of the paint.

1.6. The method of using oil-based colored thick-set paints intended for retail trade is indicated in reference Appendix 1, the density - in reference Appendix 2. (Changed edition, Amendment No. 1).

1.7. In terms of physical and chemical parameters, paints must comply with the requirements and standards specified in Table 2.

table 2

1.8. The correspondence of the changed designations of paint colors with the previously accepted ones is given in reference Appendix 3. Notes:

1. The norm for indicator 7 for a pendulum device of type TML (pendulum B) is not rejected until 01/01/95. Definition is required.

2. The norm for indicator 7 for a pendulum device of type M-3 is valid until 01/01/95. (Changed edition, Amendment No. 1).

Thickly grated colored oil paints. Specifications

current This standard applies to thickly rubbed oil colored paints, which are a paste consisting of pigments and fillers or the corresponding pigment (iron lead according to GOST 8135-74, mummy, ocher), rubbed on drying oil with or without the introduction of a drier. The paints, after being diluted with drying oil to a painting consistency, are intended for finishing work and for painting metal and wooden products used indoors and in atmospheric conditions in areas with a temperate climate. Coatings with thickly rubbed oil-based colored paints intended for use in atmospheric conditions, in two layers on metal, retain protective properties in a temperate climate for 1.5 to a point of no more than A32. Protective properties are assessed according to GOST 9.407-84. Paints are applied to the surface by brush, roller or pneumatic spraying.

SAFETY REQUIREMENTS

2.1. Paints are a fire hazardous and toxic material, which is due to the properties of the substances included in their composition: gasoline solvent for the paint and varnish industry, lead dust. Solvent vapors contained in paints have an irritating effect on the mucous membranes of the eyes, respiratory tract and skin. Lead crop causes changes in the nervous system, blood, and blood vessels.

2.2. During the production, use and testing of paints, safety and industrial sanitation rules in accordance with GOST 12.3.005-75 must be observed.

2.3. All work related to the manufacture, testing and use of paints must be carried out in rooms equipped with supply and exhaust ventilation in accordance with GOST 12.4.021-75 and fire-fighting equipment.

2.4. The maximum permissible concentrations of solvent vapors and lead compounds in the air of the working area of ​​premises, as well as the fire hazard characteristics of solvent gasoline for the paint and varnish industry are given in Table 3.

Table 3

(Changed edition, Amendment No. 1).

2.5. Persons associated with the production and use of paints must be provided with special clothing and personal protective equipment in accordance with GOST 12.4.011-89. To protect hands, pastes such as “biological gloves” should be used.

2.6. Fire extinguishing agents: sand, felt, foam, water, fire extinguishing powders.

2.7. Paint coatings after drying do not have a harmful effect on the human body.

2.8. Monitoring compliance with maximum permissible emissions (MPE) - in accordance with GOST 17.2.3.02-78. Waste disposal is carried out in accordance with the sanitary rules for the accumulation, transportation, neutralization and disposal of toxic industrial waste. (Introduced additionally, Amendment No. 1).

ACCEPTANCE

3.1. Rules for acceptance of paints - according to GOST 9980.1-86.

3.2. The need for testing according to the recommended indicators in Table 2 is established by the manufacturer and the consumer when concluding a contract for the supply of products.

3.3. Every hundredth batch is subjected to periodic testing for compliance with all requirements and standards of this standard.

3.4. If unsatisfactory results of periodic tests are obtained, the manufacturer checks each batch until satisfactory test results are obtained in a row of at least three batches. Sec. 3. (Changed edition, Amendment No. 1).

TEST METHODS

4.1. Sampling - according to GOST 9980.2-86.

4.2. Preparation of samples for testing Before testing, the paint is thoroughly mixed. The mass fraction of film-forming substances and volatile substances, as well as the degree of grinding, are determined without diluting the paint. To determine other indicators, paints are diluted to a painting consistency with drying oils in an amount of 20-30% for brands MA-015, MA-025 and 30-40% for brands MA-015 red lead, MA-015 mummy, MA-015 ocher by weight of thickly rubbed paints: paints brand MA-015, MA-015, red lead (mummy, ocher) - natural drying oil or combined K-3, K-5; MA-025 brand paints - Oxol drying oil or combined K-2. The diluted paints are filtered through a 056 N sieve (GOST 6613-86) and applied with a brush to the prepared plates. Dryer grade NF-1 (GOST 1003-73) or grade ZhK-1 is added to paint made with ocher up to 2% by weight of the paint. Plates for applying paints are prepared in accordance with GOST 8832-76, section 3. The color of the film, the drying time of the paint, the conditional light fastness of the film and its resistance to static action of water are determined on plates made of steel grades 08kp and 08ps in accordance with GOST 16523-89 or from cold-rolled steel in accordance with GOST 9045-93, size 70x150 mm and thickness 0.5-1 .0 mm or on plates made of black tin according to GOST 13345-85, size 70X150 mm and thickness 0.26-0.32 mm. Film hardness is determined on special-purpose glass plates measuring 90X120 mm and thickness 1.2 mm according to TU 21-0284461-058-90. To determine the color, the paint is applied until the substrate is completely covered and dried for 24 hours at a temperature of (20±2) °C. To determine the drying time and hardness of the film, paint is applied with a brush in one layer, to determine the conditional light resistance of the film and the resistance of the film to the static effects of water - in two layers. Each layer is dried for 24 hours at a temperature of (20±2) °C. When determining the conditional light resistance of the film, the first layer is dried at a temperature of (20±2) °C for 24 hours, the second - for 120 hours. The coating thickness of a single-layer coating after drying should be 25-30 microns, two-layer - 50-60 microns.

4.3. The color of the dried paint film is determined by visual comparison with the color of the corresponding color samples (standards) of the “Color Standard Card Files” or control color samples in natural or artificial daylight diffused light. The samples being compared should be in the same plane at a distance of 300-500 mm from the observer’s eyes at a viewing angle that excludes surface gloss. In case of disagreement in color assessment, the color determination in natural daylight is taken as the result.

4.2, 4.3. (Changed edition, Amendment No. 1).

4.4. The mass fraction of the film-forming substance in the paint is determined according to GOST 17537-72. Acetone (GOST 2768-84) or a mixture of acetone and ethyl alcohol (GOST 17299-78) in a ratio of 3:2 by volume is used as a solvent.

4.5. The mass fraction of volatile substances is determined according to GOST 17537-72. A sample weighing 1.5-2.0 g is placed in a drying oven and kept at a temperature of (140±2) °C. The first weighing is carried out after 1 hour of exposure in the cabinet, and subsequent weighings are carried out every 30 minutes until a constant weight is achieved. It is allowed to determine the mass fraction of volatile substances under an infrared lamp at a temperature of (140±2) °C. In case of disagreement in the assessment of the mass fraction of volatile substances, the final result is determination in an oven.

4.6. (Deleted, Amendment No. 1).

4.7. The conditional light resistance of the film is determined according to GOST 21903-76, method 3. The use of PRK-2 or DRT-375 lamps is allowed. The distance of the samples from the surface of the lamps should be (350±5) mm. The steady state of the lamp should be as follows: voltage (120±6) V, current (3.75±0.25) A. The film is irradiated for the time specified in clause 8 of Table 2. Irradiated samples are examined with the naked eye and compared with non-irradiated samples. Slight loss of gloss of the paint film and slight color change are acceptable. (Changed edition, Amendment No. 1).

4.8. The resistance of the film to the static effects of water is determined according to GOST 9.403-80, section. 2. Samples are placed in distilled water (GOST 6709-72) and kept in it for the time specified in paragraph 9 of Table 2. After testing, the samples are kept in air at a temperature of (20±2)°C for 2 hours and the appearance of the film is examined. After testing, the film should not peel off, wrinkle or have bubbles.

Slight loss of gloss and slight change in film color are acceptable.

4.6. (Deleted, Amendment No. 1).

4.7. The conditional light fastness of the film is determined according to GOST 21903-76, method 3.

It is allowed to use lamps of PRK-2 or DRT-375 brands. The distance of the samples from the surface of the lamps should be (350±5) mm. The steady state of the lamp should be as follows: voltage (120±6) V, current (3.75±0.25) A.

The film is irradiated for the time specified in clause 8 of the table. 2.

Irradiated samples are examined with the naked eye and compared with non-irradiated samples. Slight loss of gloss of the paint film and slight color change are acceptable.

(Changed edition, Rev.* No. 1).

4.8. The resistance of the film to the static effects of water is determined according to GOST 9.403-80, section. 2. Samples are placed in distilled water (GOST 6709-72) and kept in it for the time specified in clause 9 of the table. 2. After testing, the samples are kept in air at a temperature of (20±2)°C for 2 hours and the appearance of the film is examined.

After testing, the film should not peel off, wrinkle or have bubbles.

Slight loss of gloss and slight change in film color are acceptable.

5. PACKAGING, LABELING, TRANSPORTATION AND STORAGE

5.1. Packaging - according to GOST 9980.3-86, gr. 14.

5.2. Marking - according to GOST 9980.4-86.

When marking transport containers, the danger sign (class 3, classification code 3313) and the UN serial number 1263 must be applied according to GOST 19433-88.

5.3. Transportation and storage - according to GOST 9980.5-86.

Sec. 5. (Changed edition, Amendment No. 1).

6. MANUFACTURER WARRANTY

6.1. The manufacturer guarantees that the paints comply with the requirements of this standard subject to the conditions of transportation and storage.

6.2. Guaranteed shelf life is 12 months from the date of manufacture.

APPENDIX 1 Reference

MODE OF APPLICATION

oil-based colored thick-based paints intended for retail trade

Oil-based colored thick-rubbed paints, after being diluted with drying oil to a painting consistency, are intended for finishing work and for painting metal and wooden products used in atmospheric conditions in areas with a temperate climate and indoors.

Before use, thickly grated oil paints are diluted with drying oils in an amount of 20-30% (colored) and 30-40% (iron lead, mummy, ocher) of the mass of thickly grated paint:

paints of brands MA-015 and MA-015 (iron lead, mummy, ocher) - natural or combined drying oils K-3, K-5;

paints of the MA-025 brand ■—natural drying oils, “Oxol” or combined K-2, K-3, K-5.

Before use, it is allowed to dilute paints of the MA-015 and MA-015 red lead (mummy, ocher) with Oxol drying oil, while the paints are used only for indoor coatings.

After dilution with drying oil, the paint is, if necessary, diluted with gasoline solvent for the paint and varnish industry in an amount of no more than 5% by weight of the paint.

When using ocher, up to 2% of NF-1 or ZhK-1 drying agent by weight of paint is added.

Paints are applied to the surface with a brush, roller or paint sprayer in an even layer on a dry surface, previously cleaned of grease, dust, dirt and old peeling paint in one or two layers. Drying time for each layer at a temperature of (20±2)°C is 24 hours.

Paint consumption for single-layer coatings is 35-225 g/m2 depending on the color.

Paints are stored in tightly closed containers, protected from moisture, heat and direct sunlight.

Precautionary measures: when carrying out painting work, as well as after its completion, it is necessary to thoroughly ventilate the room; Use rubber gloves to protect your hands.

Keep away from fire.

(Changed edition, Amendment No. 1).

APPENDIX 2 Information

DENSITY OF OIL COLOR GRATED PAINTS

Paint density is 1.6-3.1 g/cm3.

The density of the film obtained after drying the paint, diluted with drying oil to a paintable consistency, is 1.4-2.5 g/cm3.

APPENDIX 3 Information

Table

compliance with changed paint color designations

(Changed edition, Amendment No. 1).

INFORMATION DATA

1. DEVELOPED AND INTRODUCED by the Ministry of Chemical Industry

DEVELOPERS

V. B. Manerov, V. M. Makarova, I. P. Gnezdova, L. V. Kozlov, V. V. Sashevsky

2. APPROVED AND ENTERED INTO EFFECT by Resolution of the USSR State Committee on Standards dated December 18, 1985 No. 4158

3. Inspection frequency: once every five years

4. INSTEAD GOST 695-7.7, GOST 8292-75 and GOST 8866-75

5. REFERENCE REGULATIVE AND TECHNICAL DOCUMENTS